DIRECTIONS: Dilute with 5 to 50 parts of water Apply working from the bottom up (Applying from the bottom up avoids streaking) Do not allow to dry on the surface Rinse area before starting on to the next area Do not use on aircraft. On anodized or highly polished aluminum, magnesium, glass or ceramic. If contact is made rinse off immediately with water.
RXSOL-16-1028-025 contains no complexing agents therefore your water treatment system can function undisturbed and optimally precipitate heavy metals.
RXSOL-16-1028-025 does not contain chlorinated hydrocarbons such as TRI - or perchlorethylene. Therefore, no closed or cooled systems are necessary for immersion cleaning.
Immersion bath: mix 1 : 5 with water, immerse parts for 10 to 60 minutes. immerse heavily soiled oil coolers, finned radiators, engine heads with radiator fins etc., for 1 to 5 hours - overnight the longest. Rinse well with high-pressure cleaner, pulse-spray or hard JET of water. Immersion bath - also in > through-feed mode< can be heated. Warm water speeds up the cleaning process. Bath temperature aprox. 40° max. 60° C. Every increase of the bath temperature by 10°C reduces the cleaning time by about half.
Example:
20°C = cleaning time aprox. 60 min.
30°C = 30 min.
40°C = 15 min.
Ultrasound bath: Ultrasound considerably speeds up the cleaning process
Fist rule: Per 100 litres of cleaning solution you need about 1 kW transmitting power. These baths can also be heated. For the external cleaning of radiator fins: First remove severe soiling with industrial vacuum.
Dilute RXSOL-16-1028-025 with water at a ration between 1 : 3 and 1 : 10, depending on the degree of soiling, apply with sprayer. Let sit for approx. 15 to20 minutes. Wash with steam cleaner or high-pressure cleaner. Clean air channels slowly and systematically with nozzle held vertically to the air fins. ( Make sure you observe instructions of the cooler manufacturer with regard to maximum pressure; otherwise the fins may bend or the radiator may be damaged. high- pressure cleaners - approx. 80 bar max. Compressed air for blasting: approx. 6 bar. ) For cleaning surfaces and appliances, depending on the degree and kind of soiling, dilute with water at a ratio of 1: 3 to 1 : 20. apply, let sit - rinse well. For cleaning anodised surfaces use a ratio of 1 : 3 to 1 : 30. For removing layers of oxidation and lightening on non-ferrous metals, use a ratio of 1 : 1 to 1 : 3. Rinse parts of surfaces well after treatment. Soiling is removed and subsequent treatment, e.g. varnishing, is not effected. A shiny gloss will appear on aluminium and brass. Copper and brass can quickly develop a natural patina. Oiling or treating with clear lacquer or with RXSOL-16-1028-025 preserves its gloss. Due to the versatile possibilities of use, our information sheets can only offer advice according to our best knowledge. We can not accept liability for damages.